Electron-Beam-Induced Current

Photo of a GaAsP-on-Si solar cell.

EBIC image of a GaAsP-on-Si solar cell revealing threading dislocations crossing the p-n junction.

One of the best ways to assess quality of semiconductor crystal quality is to use scanning electron microscopy to measure electron-beam-induced current (EBIC). In presence of an electrostatic field (p-n junction), electron-hole pairs (e-h) excited by the electron beam can be collected and the resulting current measured with a picoamplifier. EBIC provides information about the location of the junction and estimates of the diffusion length and surface recombination. EBIC mapping reveals grain boundaries and dislocations by their distinct recombination behavior. The dislocation density in semiconductors can be determined with very high precision in the 105-108 cm-2 range. EBIC observations can be performed in the JEOL 5800 at temperatures between 15 K and 300 K, which can be used to estimate the activation energy of local traps (up to 0.2-0.3 eV) or identify midgap states.

For further information, contact Mowafak Al-Jassim, 303-384-6602.